Fluxes for Submerged arc
Fused flux with very low hydrogen content for SAW welding.
Boiler works, pipes, ship building, structural steel works, tanks and pressure vessels, offshore applications etc..
Glassy melted low- manganese flux. Suitable for direct- and alternating current welding at high current up to ca 900 Ampere per wire. The flux causes slight increase of manganese and silicon in the weld, not changing Mn/Si ratio, which ensures high toughness properties of the weld metal and enables to weld plates of unlimited thickness.
Basicity: 1,05 (according to boniszewski)
Grain size: 0,32÷1,6 mm
Density: 1,4÷1,7 kg/dm3
Basicity: 1,05 (according to boniszewski)
Grain size: 0,32÷1,6 mm
Density: 1,4÷1,7 kg/dm3
- EN ISO:14174: SF CS 1 56 AC H5